Item	Unit	Opaque		Transparent		Test Methods
		Press product	Continuous press product	Press product	Continuous press product
		FMT 3331 3700	FMET 4323 4325A 4735A	FMTS 3608	FMRTS 4605
Specific Gravity	-	1.55	1.45	1.41	1.40	JIS K7112 (MOD ISO 1183)
Tensile Stress at Yield	MPa	56	58	71	68	JIS K 7162-1B/50 (IDT ISO 527-2)
Nominal Tensile Strain at Break	%	16	13	9	9	JIS K 7162-1B/50 (IDT ISO 527-2)
Modulus of Elasticity in Tension	MPa	3400	2900	3300	3100	JIS K 7162-1B/50 (IDT ISO 527-2)
Flexural Stress	MPa	78	77	94	87	JIS K 7171 (IDT ISO 178)
Flexural Modulus	MPa	3600	2900	3300	3100	JIS K 7171 (IDT ISO 178)
Chirpy Impact Strength (Notched)	kj/m2	10	5.2	1.8	1.6	JIS K 7111-1epA (MOD ISO 179)
Vicat Softening Temperature	°C	81	81	75	71	JIS K 7276 (B method) (MOD ISO306)
Temperature of Deflection under Load	°C	76	73	68	63	JIS K 7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-3	-2	-5	-3	JIS K 7133 (IDT ISO 11501)
	Latitudinal %	-2	-1	-1	-1
Flame Retardant Standards	FM 4910	Listed	Listed	Listed	Listed	FM4910
	UL94	V-0	V-0	-	-	UL94
Total Light Transmittance	%	-	-	75	77	JIS K7361-1

Item	Unit	Opaque			Transparent	Test Methods
		FMH 5300	FMH 5305	FMHL 5710 Combination with PVC as a Surface and C-PVC as a core material	FMHS 6650
Specific Gravity	-	1.75	1.55	1.63	1.46	JIS K7112 (MOD ISO 1183)
Tensile Stress at Yield	MPa	54	63	55	74	JIS K 7162-1B/50 (IDT ISO 527-2)
Nominal Tensile Strain at Break	%	23	20	22	12	JIS K 7162-1B/50 (IDT ISO 527-2)
Modulus of Elasticity in Tension	MPa	3300	3000	3300	3300	JIS K 7162-1B/50 (IDT ISO 527-2)
Flexural Stress	MPa	81	88	83	99	JIS K 7171 (IDT ISO 178)
Flexural Modulus	MPa	3300	3000	3300	3300	JIS K 7171 (IDT ISO 178)
Chirpy Impact Strength (Notched)	kj/m2	12	7.2	8.4	1.6	JIS K 7111-1epA (MOD ISO 179)
Vicat Softening Temperature	°C	105	97	Not Application	94	JIS K 7276 (B method) (MOD ISO306)
Temperature of Deflection under Load	°C	94	86	85	85	JIS K 7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-3	-4	-3	-5	JIS K 7133 (IDT ISO 11501)
	Latitudinal %	-2	-1	-2	0.5
Flame Retardant Standards	FM 4910	Listed	Listed	Listed	Listed	FM4910
	UL94	V-0	-	V-0	-	UL94
Total Light Transmittance	%	-	-	-	71	JIS K7361-1

Item	Unit	PVC		CPVC		Test Methods
		Press product	Continuous press product	Press product
		FMND 7708(Clear)	FMND 74605(Clear)	FMND 7605(Clear)	FMND MR760
Specific Gravity	-	1.40	1.40	1.46	1.56	JIS K7112 (MOD ISO 1183)
Tensile Stress at Yield	MPa	72	68	72	74	JIS K 7162-1B/50 (IDT ISO 527-2)
Nominal Tensile Strain at Break	%	8	-	14	12	JIS K 7162-1B/50 (IDT ISO 527-2)
Modulus of Elasticity in Tension	MPa	3300	-	3000	3000	JIS K 7162-1B/50 (IDT ISO 527-2)
Flexural Stress	MPa	98	87	93	98	JIS K 7171 (IDT ISO 178)
Flexural Modulus	MPa	3300	3100	3000	3200	JIS K 7171 (IDT ISO 178)
Chirpy Impact Strength (Notched)	kj/m2	2	1.8	1.7	1.6	JIS K 7111-1epA (MOD ISO 179)
Vicat Softening Temperature	°C	75	71	94	94	JIS K 7276 (B method) (MOD ISO306)
Temperature of Deflection under Load	°C	69	63	85	85	JIS K 7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-5	-3	-5	-5	JIS K 7133 (IDT ISO 11501)
	Latitudinal %	-1	-1	1	-1
Flame Retardant Standards	FM 4910	Listed	Listed	Listed	Listed	FM4910
	UL94	-	-	V-0, 5VA(7606 only)	-	UL94
Total Light Transmittance	%	67	70	63	60	JIS K7361-1

Item	Unit	FMPVDF F300	Test Methods
Specific Gravity	-	1.78	JIS K7112 (MOD ISO 1183)
Tensile Stress at Yield	MPa	53	JIS K 7162-1B/50 (IDT ISO 527-2)
Nominal Tensile Strain at Break	%	15	JIS K 7162-1B/50 (IDT ISO 527-2)
Flexural Stress	MPa	64	JIS K 7171 (IDT ISO 178)
Flexural Modulus	MPa	1800	JIS K 7171 (IDT ISO 178)
Chirpy Impact Strength (Notched)	kj/m2	10	JIS K 7111-1epA (MOD ISO 179)
Vicat Softening Temperature	°C	165	JIS K 7276 (B method) (MOD ISO306)
Temperature of Deflection under Load	°C	140	JIS K 7191
Flame Retardant Standards	FM 4910	Listed	FM4910
	UL94	-	UL94