Lead-free PVC Materials | TAKIRON Co.,LTD.

Item	Unit	General Grade								Test method
Item	Unit	TS608	RTS1100	ESS8800A	TSP338	RTSP1330	ETSP1380	T938	ET1980	Test method
Color		Transparent			Ivory			Gray		-
Specific Gravity	—	1.4	1.4	1.4	1.39	1.45	1.45	1.39	1.45	JIS K7112(MOD ISO 1183)
Tensile Stress at Yield	MPa	75	74	67	60	58	58	60	58	JIS K7162-1B/50(IDT ISO 527-2)
Nominal Tensile Strain at Break	%	8	8	15	12	20	20	12	20	JIS K7162-1B/50(IDT ISO 527-2)
Modulus pf Elasticity in Tension	MPa	3400	3200	3100	3000	3100	2800	3000	2800	JIS K7162-1B/1(IDT ISO 527-2)
Flexural Stress	MPa	107	104	—	81	83	80	81	80	JIS K7171(IDT ISO 178)
Flexural Modulus	MPa	3600	3500	—	2800	3000	3600	2800	3600	JIS K7171(IDT ISO 178)
Chirpy Impact Strength(Notched)	KJ/m²	2.1	1.8	1.7	10	4.2	7.4	10	7.4	JIS K7111-1epA(MOD ISO 179)
Vicat Softening Temperature	°C	71	70	67	80	81	81	80	81	JIS K7206(B method)(MOD ISO306)
Temperature of Deflection under load	°C	63	62	—	74	75	75	74	75	JIS K7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-5	-2	-3.7	-3	-2	-3	-3	-3	JIS K7133(IDT ISO 11501)
Dimensional Change on Heating (140°C, 55min)	Latitudinal %	-1	-1	-0.7	-2	-1	-1	-2	-1	JIS K7133(IDT ISO 11501)
Total Light transmittance	%	85	86	—	—	—	—	—	—	JIS K7361-1(IDT ISO 13468-1)

The above data are typical test results(iof 5mm thick specmine) and here without guarantee.

Item	Unit	Heat Resisitance Grade			High Impact Grade		Test method
Item	Unit	HTS625	FMH5305	HT928	TSHI601HI	THQ098	Test method
Color		Transparent	Ivory	Dark Gray	Transparent	Dark Gray	—
Specific Gravity	—	1.55	1.55	1.51	1.32	1.33	JIS K7112(MOD ISO 1183)
Tensile Stress at Yield	MPa	70	71	65	53	48	JIS K7162-1B/50(IDT ISO 527-2)
Nominal Tensile Strain at Break	%	15	12	21	15	74	JIS K7162-1B/50(IDT ISO 527-2)
Modulus pf Elasticity in Tension	MPa	3200	3100	3000	2500	2300	JIS K7162-1B/1(IDT ISO 527-2)
Flexural Stress	MPa	98	98	90	73	61	JIS K7171(IDT ISO 178)
Flexural Modulus	MPa	3200	3200	3100	2600	2200	JIS K7171(IDT ISO 178)
Chirpy Impact Strength(Notched)	KJ/m²	2.2	2.2	6	58	80	JIS K7111-1epA(MOD ISO 179)
Vicat Softening Temperature	°C	99	98	104	71	78	JIS K7206(B method)(MOD ISO306)
Temperature of Deflection under load	°C	88	88	94	66	72	JIS K7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-5	-5	-5	-4	-3	JIS K7133(IDT ISO 11501)
Dimensional Change on Heating (140°C, 55min)	Latitudinal %	-1	-2	-1	-2	-2	JIS K7133(IDT ISO 11501)
Total Light transmittance	%	58	—	—	72	—	JIS K7361-1(IDT ISO 13468-1)

The above data are typical test results(of 5mm thick specmine) and here without guarantee.

Item	Unit	FM Flame Retardant			Static Dissipative		Metal Free		Test method
Item	Unit	FMHS6650	FMTS3608	FMET4325	TND77665	TND77348	TMC60601	TMC60331	Test method
Color		Trans -parent		Ivory	Trans -parent	Ivory	Trans -parent	Ivory	—
Specific Gravity	—	1.46	1.41	1.45	1.4	1.39	1.4	1.4	JIS K7112(MOD ISO 1183)
Tensile Stress at Yield	MPa	74	71	58	74	60	75	57	JIS K7162-1B/50(IDT ISO 527-2)
Nominal Tensile Strain at Break	%	12	9	13	7	8	7	20	JIS K7162-1B/50(IDT ISO 527-2)
Modulus pf Elasticity in Tension	MPa	3300	3300	2900	3300	3000	3500	2800	JIS K7162-1B/1(IDT ISO 527-2)
Flexural Stress	MPa	99	94	77	98	81	102	79	JIS K7171(IDT ISO 178)
Flexural Modulus	MPa	3300	3300	2900	3400	2800	3600	2800	JIS K7171(IDT ISO 178)
Chirpy Impact Strength(Notched)	KJ/m²	1.6	1.8	5.2	2.3	10	2.3	7.3	JIS K7111-1epA(MOD ISO 179)
Vicat Softening Temperature	°C	94	75	81	72	80	74	77	JIS K7206(B method)(MOD ISO306)
Temperature of Deflection under load	°C	85	68	73	65	74	68	68	JIS K7191
Dimensional Change on Heating (140°C, 55min)	Longitudinal %	-5	-5	-2	-6	-3	-5	-6	JIS K7133(IDT ISO 11501)
Dimensional Change on Heating (140°C, 55min)	Latitudinal %	0.5	-1	-1	-1	-2	-1	-1	JIS K7133(IDT ISO 11501)
Total Light transmittance	%	71	75	—	77	—	83	—	JIS K7361-1(IDT ISO 13468-1)

The above data are typical test results(of 5mm thick specmine) and here without guarantee.

Item	Unit	ROD		Test method
Item	Unit	NC ROD	ROD938 Less than ø100	Test method
Color		Ivory	Gray	—
Tensile Stress at Yield	MPa	57	55	JIS K7162-1B/50(IDT ISO 527-2)
Nominal Tensile Strain at Break	%	10	14	JIS K7162-1B/50(IDT ISO 527-2)
Flexural Stress	MPa	87	83	JIS K7171(IDT ISO 178)
Flexural Modulus	MPa	3400	3300	JIS K7171(IDT ISO 178)
Chirpy Impact Strength(Notched)	KJ/m²	6	3	JIS K7111-1epA(MOD ISO 179)
Vicat Softening Temperature	°C	75	75	JIS K7206(B method)(MOD ISO306)

The above data are series of test results with 5 mm thick specimens, cut from individual ROD, and given here without guarantee.

Item	Unit	WELDING ROD			Test method
Item	Unit	8061	338S	938S	Test method
Color		Transparent	Ivory	Gray	—
Tensile Stress at Yield	MPa	62	68	68	JIS K7162
Nominal Tensile Strain at Break	%	5	10	10	JIS K7162
Chirpy Impact Strength(Notched)	KJ/m²	2	2	2	JIS K7111
Vicat Softening Temperature	°C	71	71	71	JIS K7206

The above data are series of test results with 5 mm thick specimens, knead from individual WELDING ROD, and given here without guarantee.