| Testing Items | group |
PVC |
Poly-carbonate |
PETG |
Test Methods |
| color |
Trans
parent |
ivory |
Trans
parent |
FM Trans
parent |
FM Trans
parent |
FM Trans
parent |
Trans
parent |
Trans
parent |
Trans
parent |
| unit |
TND |
TND |
ESND |
FMND |
FMND |
FMND |
PCNDL |
PETND MR |
PETND- |
| code |
77665 |
77348 |
47800 |
7708 |
7605 |
MR760 |
77810 |
G60 |
76600 |
| Lead Free | |
Yes |
Yes |
Yes |
Yes |
Yes |
Yes |
- |
- |
- |
|
| Specific Gravity | |
1.40 |
1.39 |
1.40 |
1.41 |
1.46 |
1.46 |
1.20 |
1.27 |
1.27 |
JIS
K 7112
(MOD ISO 1183) |
Tensile Stress
at Yield | MPa |
74 |
60 |
73 |
72 |
72 |
74 |
65 |
52 |
52 |
JIS
K 7162-1B/50
(IDT ISO 527-2) |
Nominal Tensile
Strain at Break | % |
7 |
8 |
7 |
8 |
15 |
12 |
83 |
28 |
28 |
JIS
K 7162-1B/50
(IDT ISO 527-2) |
Modulus of Elasticity
in Tension | MPa |
3,300 |
3,000 |
3,200 |
3,300 |
3,000 |
3,000 |
2,300 |
2,000 |
2,000 |
JIS
K 7162-1B/1
(IDT ISO 527-2) |
Chirpy Impact
Strength (Notched) |
kJ/m2 |
2.3 |
6 |
1.8 |
2.0 |
1.7 |
1.6 |
15.0 |
6.4 |
6.4 |
JIS
K 7111-lepA
(IDT ISO 179) |
| Flexural Stress | MPa |
98 |
81 |
104 |
98 |
93 |
98 |
90 |
71 |
71 |
JIS
K 7171
(IDT ISO 178) |
| Flexural Modulus | MPa |
3,400 |
2,800 |
3,500 |
3,300 |
3,000 |
3,200 |
2,300 |
2,000 |
2,000 |
JIS
K 7171
(IDT ISO 178) |
Temperature of
Deflection under Load | °C
(1.80MPa) | 65 |
74 |
62 |
69 |
85 |
85 |
140 |
69 |
69 |
JIS
K 7191 |
Vicat Softening
Temperature | °C
(method B) | 72 |
80 |
70 |
75 |
94 |
94 |
148 |
74 |
74 |
JIS
K 7206
(MOD ISO 306) |
Dimensional Change
on Heating | %
(longitudinal) | -6 |
-3 |
-3 |
-5 |
-5 |
-5 |
- |
- |
-3 |
JIS
K 7133(IDT
ISO 11501) |
%
(latitudinal) | -1 |
-2 |
-1 |
-1 |
-2 |
-2 |
- |
- |
-0.5 |
| Surface Resistivity |
Ω/□ |
106∼8 |
JIS K 6911 |
| Volume Resistivity |
Ω⋅m |
1013 and higher |
JIS K 6911 |
|
| The above data are a series of test
results with 5 mm thick specimen and given here without gurantee. |
|